We are ranked amongst the foremost firms that are engaged in manufacturing and supplying a superior quality AF C 350 Non Asbestos Jointing Gasket Sheets. These sheets are a standard sealing material used in compressors, pipelines, transmission, gas meters and internal combustion engines. Also, AF C 350 Non Asbestos Jointing Gasket Sheets are available in different specifications as per clients’ requirements.
| Properties | Testing Method | Unit | Specification |
| Density | ASTM F 1315 | G/cm3 | 1.6-1.9 |
| Compressibility | ASTM F 36J | % | 7-17 |
| Recovery | ASTM F 36 J | % | 40 |
| Tensile Strength (Across Grain) | ASTM F 152 | N/mm2 | 8 |
| Stress Relaxation | DIN 52913 | | |
| a. 16 hours, 175°C | 50 Mpa | Mpa | 30 |
| b. 16 hours, 300°C | 50 Mpa | Mpa | 20 |
| Gas Solubility (0.80 mm) | ASTM F 37 B | M/hour | 1.0 |
| Cold/Hot Compression (0.80 mm) | | | |
| a. Thickness decrease at 23°C | | % | |
| b. Thickness decrease at 300°C | | | |
| ASTM OIL NO 3 (5 HRS, 150°C) | | | |
| Thickness Increase | | % | 10 |
| Weight Increase | | % | 10 |
| 10. Fuel B (5 hrs, 23°C) | | | |
| Thickness Increase | | % | 10 |
| Weight Increase | | % | 10 |
| 11. Water (5 hrs, 100°C) | | | |
| Thickness Increase | | % | 10 |
| Weight Increase | | % | 10 |
| 12. Thickness Increase | | | |
| 65% H2S04 Acid (48 hrs, 23°C) | | % | |
| 96% H2S04 Acid (48 hrs, 23°C) | | % | |
| 40% HNO3 Acid (48 hrs, 23°C) | | % | |
| ASTM Line call out | | | ASTM 104 F712911E12A964M9 |
| Max. Operating Conditions | | | |
| Max. Peak Temperature | | ºC | 400 |
| Max. Operating Temperature | | ºC | 350 |
| Max. Operating Pressure | | Bar | 100 |