- Kilograms/Kilograms
- 100
- Kilograms/Kilograms,
- Jointing Gasket Sheets
- Sheets
- Non Asbestos
- 0.25 to 6 Millimeter (mm)
With a vision to serve clients in best possible manner, we have been engaged in offering quality approved AF Oil Steel 350 Non Asbestos Jointing Gasket Sheets. These sheets are developed by using top-notch materials under proper guidance of dexterous professionals. Also, AF Oil Steel 350 Non Asbestos Jointing Gasket Sheets are suitable to seal off hydraulic, engines, transmission and refrigerating oils as well as other hydrocarbons..
| Properties | Testing Method | Unit | Specification |
| Density | ASTM F 1315 | G/cm3 | 1.7-2.0 |
| Compressibility | ASTM F 36J | % | 7-17 |
| Recovery | ASTM F 36 J | % | 40 |
| Tensile Strength (Across Grain) | ASTM F 152 | N/mm2 | 13.7 |
| Stress Relaxation | DIN 52913 | | |
| a. 16 hours, 175°C | 50 Mpa | Mpa | 25 |
| b. 16 hours, 300°C | 50 Mpa | Mpa | |
| Gas Solubility (0.80 mm) | ASTM F 37 B | M/hour | 1.0 |
| Cold/Hot Compression (0.80 mm) | | | |
| a. Thickness decrease at 23°C | | % | |
| b. Thickness decrease at 300°C | | | |
| ASTM OIL NO 3 (5 HRS, 150°C) | | | |
| Thickness Increase | | % | 10 |
| Weight Increase | | % | 10 |
| 10. Fuel B (5 hrs, 23°C) | | | |
| Thickness Increase | | % | 10 |
| Weight Increase | | % | 10 |
| 11. Water (5 hrs, 100°C) | | | |
| Thickness Increase | | % | 10 |
| Weight Increase | | % | 10 |
| 12. Thickness Increase | | | |
| 65% H2S04 Acid (48 hrs, 23°C) | | % | |
| 96% H2S04 Acid (48 hrs, 23°C) | | % | |
| 40% HNO3 Acid (48 hrs, 23°C) | | % | |
| ASTM Line call out | | | ASTM 104 F712911E12A964M6 |
| Max. Operating Conditions | | | |
| Max. Peak Temperature | | ºC | 400 |
| Max. Operating Temperature | | ºC | 300 |
| Max. Operating Pressure | | Bar | 120 |
- Cheque, Cash in Advance (CID)
- 600000 Per Month
- 10 Days
- All India
Village Galand, Dibarsi Road, Jindal Nagar, Hapur Uttar Pradesh India +918037303894
Phone :+918037303894